Antioxidant, UV Absorber And Pigment For LLDPE

LLDPE is an abbreviation of Low-density polyethylene (LLDPE) is a thermoplastic made of the monomer ethylene.

LLDPE is used in the production of plastic film for packaging, mulch and greenhouse film for agriculture.

The processing temperature of LLDPE range is 220-240℃.

 

Antioxidant For LLDPE

Antioxidant 1010 + antioxidant 168 is recommended in LLDPE. To avoid blooming, the dosage of antioxidant is suggested below 0.1%.

 

UV Absorber/ HALS For LLDPE

HALS 622 or HALS 944 + UV 531 is recommended in LLDPE processing.

 

Optical Brightener For LLDPE

Application OBAs Adding Form Typical OBAs Issue to mind
Polyolefin Dry powder mix FP 127

KSN

Compatibility

PP>hdpe>ldpe

Immigration resistance

 

Pigment for LLDPE (please click on title)

 

Things to know when selecting pigments for polyolefins

1. Distortion & Shrinkage 

A number of organic pigments cause distortion in certain types of polyolefins, especially in HDPE. These pigments also enhance the shrinkage of polyolefins, particularly in the direction of the flow.

2. Dispersibility 

The dispersibility of an organic pigment which is to be incorporated in a polyolefin is of particular importance. This is especially true for the coloration of extrusion films and for HDPE or PP ribbon made from stretched blown film or from sheeted extrusion film, as well as for the coating or melt spin dyeing. Powder form pigment dispersion is not adequate in these applications. Poor dispersion causes filler specks, holes in films, and other faults. Pigment preparations, usually in combination with polyolefins as a carrier, are frequently used to color polyolefins.

Pigment powders continue to be used in thick-walled articles, such as extruded sheets, or hollow objects, or in injection-molded products; although color concentrates are beginning to be more important even in these areas.

Pigment and polyolefin paste preparations containing between 20 and 70% pigment are also used. They are manufactured by means of three-roll mills, agitated ball mills, or dissolves or similar equipment. Such preparations are employed primarily to produce bottles, injection-molded articles, or extrusion sheets. These preparations have the advantage of being applicable in volumetric doses and may be premixed in slow mixers or gravitation mixers to uniformly adhere to the plastic granulate.