Polyamide Impact Modifier BX CA EPDM Grafted Maleic Anhydride

Description

BX CA EPDM is prepared by EPDM reaction grafting maleic anhydride because it introduces a strongly polar side group (maleic anhydride) on the main chain of EPDM molecules, so maleic anhydride grafted EPDM can be a bridge to enhance the adhesion and compatibility of polar materials and non-polar materials. In the application of nylon + glass fiber modification, it can react with the surface-treated glass fiber to improve the compatibility of nylon with glass fiber, thereby improving the tensile strength and impact strength of nylon. BX CA EPDM can be used both as a compatibilizer and as a flexibilizer, as a nylon compatibilizer it is also suitable for PA/PE, PA/PP alloy, which can improve the toughness of the alloy, BX CA EPDM as a nylon toughening agent, its low-temperature toughness and fatigue resistance are very superior

Synonyms

maleic anhydride grafted EPDM;

 

The principle of nylon toughening

EPDM elastomer grafted maleic anhydride in the toughening role is the elastomer part, the higher the proportion of addition, the better the toughening effect, usually can not exceed 20%, and the main role of the active port of maleic anhydride is to connect with nylon, the closed loop of maleic anhydride meets the amino group of nylon, the closed loop opens, the amino group of the access nylon reacts to link, and generates water molecules, so the role of the elastomer part is toughening, and the role of the maleic anhydride group is compatible.

 

PE Grafted Maleic Anhydride Application

1. It can be used as a compatibilizer between nylon and glass fiber;
2. It can be used as a nylon flexibilizer;
3. It can improve the adhesion between nylon and polar materials.

Properties

This data is derived from the average value of product retention samples within half a year, and this data is updated every six months. The grafting rate standard is: <0.4% low; Medium 0.4%-0.8%; ≥0.8% high.

Test the project Test data Detection method
density 0.87 g/cm³ ASTM D792  ISO 1183
Melting fingers 0.1-0.4（190℃，2.16kg）g/10min ASTM D1238  ISO 1133
Grafting rate high Acid-base titration
appearance grain

Performance Test Data

PA6 toughening Test raw material: PA6 (YH800) Test equipment: 35-type twin screw extrusion granulator

performance unit PA6 PA6+15%

BX CA EPDM

 PA6+20%

BX CA EPDM
Tensile strength MPa 60 55 50
Bending strength MPa 90 80 70
Cantilever impact strength J/M 80 700 1000

PA66 toughening Test raw material: PA66 (ERP27) Test equipment: 35-type twin screw extrusion granulator

performance unit PA66 PA66+15% BX CA EPDM PA66+20% BX CA EPDM
Tensile strength MPa 75 57 55
Bending strength MPa 102 85 80
Cantilever impact strength J/M 80 800 1000

PA6+GF test raw materials: PA6 (YH800), glass fiber (Boulder 988A); Test equipment: 35 type twin screw extrusion granulator

performance unit PA6 PA6+30%GF+6% BX CA EPDM
Tensile strength MPa 60 135
Bending strength MPa 90 195
Cantilever impact strength J/M 80 250

PA66+GF test raw materials: PA66 (ERP27), glass fiber (Boulder 988A); Test equipment: 35 type twin screw extrusion granulator

performance unit PA66 PA66+25%GF+8% BX CA EPDM
Tensile strength MPa 75 150
Bending strength MPa 102 215
Cantilever impact strength J/M 80 200

25kg per bag.